Koliko vpliva ima material za ogrevalno žico na življenjsko dobo električne ogrevalne cevi?

Material ogrevalne žice je ključni dejavnik, ki vpliva na življenjsko dobo električne ogrevalne cevi . Različni materiali imajo razlike v visoki temperaturni upornosti, oksidacijski upornosti, korozijski upornosti, mehanski moči itd. ., kot sledi:
Visoka temperaturna odpornost
Nickel-chromium alloy: such as Cr20Ni80 and other models, with a high melting point, can work stably for a long time at high temperatures of 1000℃- 1200℃. Its crystal structure is relatively stable at high temperatures, and it is not easy to deform and crack due to thermal stress, so it can effectively extend the service life of the electric heating Tube .
Fe-Cr-Aluminum alloy: represented by 0Cr25Al5, the melting point is also relatively high, generally around 1300℃. However, its strength at high temperature is slightly lower than that of nickel-chromium alloy. When it is in a high temperature environment for a long time, the grain growth may occur, causing the heating wire to become brittle, Vpliva na življenjsko dobo električne ogrevalne cevi ., če pa se uporablja v srednjem temperaturnem okolju (800 stopinj - 1000), lahko še vedno ohrani dobro zmogljivost in dolgo življenjsko dobo .
Molibdenska žica in volframova žica: Tališča teh dveh materialov so izredno visoka, pri čemer je tališče molibdenske žice približno 2620 stopinj in tališče volframa, ki je visoka 3410 stopinj ., se pogosto uporabljajo v izjemno visokih zahtevah in drugih celicah z izjemno visokimi cenami, ki so zelo visoke temperature, in druga celica z izjemno visokimi cenami, ki so na primer z visoko temperaturo, in druga cena z izjemno visokimi zahtevami, ki so na primer z visokimi celicami, in druga celica z izjemno visokimi zahtevami, ki so na primer z visoko temperaturo, in druga celica z izjemno visokimi zahtevami, ki so na primer z visoko temperaturo, in drugim. Okolje lahko ohranijo dobro stabilnost in imajo dolgo življenjsko dobo ., vendar jih je enostavno oksidirati pri visokih temperaturah in jih je treba na splošno uporabiti pod vakuumsko ali inertno zaščito plina, sicer jih bo z oksidacijo hitro poškodoval .
Učinkovitost antioksidacije
Nikelj-kromijeva zlitina: na površini se lahko oblikuje gost oksidni film, kar lahko prepreči, da bi se notranja kovina še dodatno oksidirala in ima dobre antioksidacijske zmogljivosti . v običajnih pogojih uporabe, lahko učinkovito prepreči, da bi ogrevalna žica postala tanjša in se lomi zaradi oksidacije, s čimer se je v službi podaljšala z električno ogrevalno cev
Iron-chromium-aluminum alloy: Although it can also form an oxide film, its oxide film is slightly less dense than that of nickel-chromium alloy. In an environment with high temperature, high humidity or corrosive gas, the oxidation rate of the iron-chromium-aluminum alloy heating wire may accelerate, resulting in a shortened service life.
Učinkovitost antikorozije
Nikelj-kromium zlitina: ima določeno odpornost na nekatere korozivne medije, kot so kisline in alkalis . v nekaterih nestrokovno korozivnih okoljih, ogrevalne žice z nickel-kromijevimi zlitina
Iron-chromium-aluminum alloy: The corrosion resistance is relatively weak, especially in strong acidic or alkaline environments, it is easy to be corroded, resulting in damage to the heating wire. Therefore, in an environment with corrosive media, it is generally not recommended to use electric heating tubes with iron-chromium-aluminum alloy heating wires, otherwise it will significantly shorten its storitveno življenje .
Mehanska trdnost
Nikelj-kromium zlitina: ima dobro žilavost in mehansko trdnost in ga ni enostavno razbiti, če je podvrženo določenim učinkom zunanje sile ali spremembam toplotnega napetosti . To omogoča ogrevalno žico, da med namestitvijo in uporabi električne ogrevalne cevi prenesejo določene napetosti in se ne morejo poškodovati rahle vibracije ali shranjevanja, ki jih rahlo vibrira ali pa se rahlo vibrira ali pa se z rahlo vibriranjem ali termičnima iztegnitva Življenje .
Zlitina železa-kromium-aluminije: Mehanska trdnost je razmeroma nizka, še posebej po dolgotrajni uporabi pri visokih temperaturah je enostavno postati krhka in enostavno razbiti, če je podvržena učinku zunanje sile ., če pri uporabi električnih ogrevalnih cevi z železno-kromijevimi zlitinami, ki jih je treba plačati, da bi se lahko izognili hudi prekinite in preprečite električno ogrevalno cev .